§1065.1113. General provisions related to vanadium sublimation temperatures in SCR catalysts.
40 C.F.R. § 1065.1113
Sections 1065.1113 through 1065.1121 specify procedures for determining vanadium emissions from a catalyst based on catalyst temperature. Vanadium can be emitted from the surface of SCR catalysts at temperatures above 550 °C, dependent on the catalyst formulation. These procedures are appropriate for measuring the vanadium sublimation product from a reactor by sampling onto an equivalent mass of alumina and performing analysis by Inductively Coupled Plasma—Optical Emission Spectroscopy (ICP-OES). Follow standard analytic chemistry methods for any aspects of the analysis that are not specified.
The procedure is adapted from “Behavior of Titania-supported Vanadia and Tungsta SCR Catalysts at High Temperatures in Reactant Streams: Tungsten and Vanadium Oxide and Hydroxide Vapor Pressure Reduction by Surficial Stabilization” (Chapman, D.M., Applied Catalysis A: General, 2011, 392, 143-150) with modifications to the acid digestion method from “Measuring the trace elemental composition of size-resolved airborne particles” (Herner, J.D. et al, Environmental Science and Technology, 2006, 40, 1925-1933).
Laboratory cleanliness is especially important throughout vanadium testing. Thoroughly clean all sampling system components and glassware before testing to avoid sample contamination.
Notes, amendments, and revision history
Source
Source: Sections 1065.1113 through 1065.1119 appear at 88 FR 4691, Jan. 24, 2023, unless otherwise noted.
Source
Source: 79 FR 23820, Apr. 28, 2014, unless otherwise noted.
Authority
Authority: 42 U.S.C. 7401-7671q.
Source
Source: 70 FR 40516, July 13, 2005, unless otherwise noted.